Aclar® UltRx 6000 film is a 6.00 mil (152 µm) PCTFE homopolymer, high performance barrier filmfor the pharma and medical markets. It thermoforms well on conventional blister packagingequipment and provides the highest barrier of any clear film.
Please sign in to access more documents
Once signed in, you may be able to access additional documents for your account.
Properties
- Crystalline Melting Point
- 211 °C, ASTM D4591
- 412 °F, ASTM D4591
- Dimensional Stability
- <= +2% MD, 10 min at 300 °F/149 °C, ASTM D1204
- <= -2% TD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 150 - 225% MD/TD, ASTM D882
- Haze
- < 1%, ASTM D1003
- Modulus
- 1103 - 1379 MPa MD/TD Secant, ASTM D882
- 160000 - 200000 psi MD/TD Secant, ASTM D882
- Oxygen Transmission Rate
- 0.63 cc/100in²/day-atm at 73 °F (23 °C), 65% RH, ASTM D3985
- 1.78 cc/100in²/day-atm at 104 °F (40 °C), 75% RH, ASTM D3985
- 27.6 cc/m²/day-atm at 104 °F (40 °C), 75% RH, ASTM D3985
- 9.77 cc/m²/day-atm at 73 °F (23 °C), 65% RH, ASTM D3985
- Specific Gravity
- 2.11, ASTM D1505
- Surface Tension
- >= 42 dynes/cm (Treated Side), ASTM D2578
- Tensile Strength
- 28 - 48 MPa MD/TD, ASTM D882
- 4000 - 7000 psi MD/TD, ASTM D882
- Water Vapor Transmission Rate
- 0.0003 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0005 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.002 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.0025 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- 0.0047 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0078 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.0302 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.038 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 2180 in²/lb
- 3.10 m²/kg
Notes
- Test Conditions
- Test conditions for properties are 73°F, 50% RH unless otherwise noted
Sampling
- Sample Products
- Yes
Properties
- Crystalline Melting Point
- 211 °C, ASTM D4591
- 412 °F, ASTM D4591
- Dimensional Stability
- <= +2% MD, 10 min at 300 °F/149 °C, ASTM D1204
- <= -2% TD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 150 - 225% MD/TD, ASTM D882
- Haze
- < 1%, ASTM D1003
- Modulus
- 1103 - 1379 MPa MD/TD Secant, ASTM D882
- 160000 - 200000 psi MD/TD Secant, ASTM D882
- Oxygen Transmission Rate
- 0.63 cc/100in²/day-atm at 73 °F (23 °C), 65% RH, ASTM D3985
- 1.78 cc/100in²/day-atm at 104 °F (40 °C), 75% RH, ASTM D3985
- 27.6 cc/m²/day-atm at 104 °F (40 °C), 75% RH, ASTM D3985
- 9.77 cc/m²/day-atm at 73 °F (23 °C), 65% RH, ASTM D3985
- Specific Gravity
- 2.11, ASTM D1505
- Surface Tension
- >= 42 dynes/cm (Treated Side), ASTM D2578
- Tensile Strength
- 28 - 48 MPa MD/TD, ASTM D882
- 4000 - 7000 psi MD/TD, ASTM D882
- Water Vapor Transmission Rate
- 0.0003 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0005 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.002 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.0025 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- 0.0047 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0078 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.0302 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.038 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 2180 in²/lb
- 3.10 m²/kg
Notes
- Test Conditions
- Test conditions for properties are 73°F, 50% RH unless otherwise noted
Sampling
- Sample Products
- Yes
- Yield : 2180 in²/lb|3.10 m²/kg
- Tensile Strength : 28 - 48 MPa MD/TD, ASTM D882|4000 - 7000 psi MD/TD, ASTM D882
- Haze : < 1%, ASTM D1003
- Modulus : 1103 - 1379 MPa MD/TD Secant, ASTM D882|160000 - 200000 psi MD/TD Secant, ASTM D882
- Elongation : 150 - 225% MD/TD, ASTM D882
- Water Vapor Transmission Rate : 0.0003 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249|0.0005 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249|0.002 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249|0.0025 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249|0.0047 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249|0.0078 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249|0.0302 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249|0.038 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Specific Gravity : 2.11, ASTM D1505
- Oxygen Transmission Rate : 0.63 cc/100in²/day-atm at 73 °F (23 °C), 65% RH, ASTM D3985|1.78 cc/100in²/day-atm at 104 °F (40 °C), 75% RH, ASTM D3985|27.6 cc/m²/day-atm at 104 °F (40 °C), 75% RH, ASTM D3985|9.77 cc/m²/day-atm at 73 °F (23 °C), 65% RH, ASTM D3985
- Crystalline Melting Point : 211 °C, ASTM D4591|412 °F, ASTM D4591
- Surface Tension : >= 42 dynes/cm (Treated Side), ASTM D2578
- Dimensional Stability : <= +2% MD, 10 min at 300 °F/149 °C, ASTM D1204|<= -2% TD, 10 min at 300 °F/149 °C, ASTM D1204
- Test Conditions : Test conditions for properties are 73°F, 50% RH unless otherwise noted