Aclar® Barrier Films
Aclar UltRx 3000 (3.00 Mil/76 μm)
Aclar® UltRx 3000 is a 3.00 mil (76 µm) PCTFE homopolymer, high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister pack- aging equipment and provides the best barrier of any clear film.
Properties
- Crystalline Melting Point
- 211 °C, ASTM D4591
- 412 °F, ASTM D4591
- Dimensional Stability
- < -6% TD, 10 min at 300 °F/149 °C, ASTM D1204
- <= +6% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 150 - 225% MD, ASTM D882
- 175 - 225% TD, ASTM D882
- Haze
- < 1%, ASTM D1003
- Modulus
- 1103 - 1379 MPa MD/TD Secant, ASTM D882
- 160,000 - 200,000 psi MD/TD Secant, ASTM D882
- Specific Gravity
- 2.11, ASTM D1505
- Surface Tension
- >= 42 dynes/cm (Treated Side), ASTM D2578
- Tensile Strength
- 28 - 48 MPa TD, ASTM D882
- 4000 - 7000 psi TD, ASTM D882
- 41 - 62 MPa MD, ASTM D882
- 6000 - 9000 psi MD, ASTM D882
- Water Vapor Transmission Rate
- 0.0008 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0015 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.0016 gms/100in²/day at 86 °F (30 °C), 60% RH, ASTM F1249
- 0.004 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.0057 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- 0.009 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.015 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.016 gms/m²/day at 86 °F (30 °C), 60% RH, ASTM F1249
- 0.048 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.065 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 4,380 in²/lb
- 6.23 m²/kg
Notes
- Test Conditions
- Test conditions for properties are 73°F, 50% RH unless otherwise noted
Sampling
- Sample Products
- Yes
Properties
- Crystalline Melting Point
- 211 °C, ASTM D4591
- 412 °F, ASTM D4591
- Dimensional Stability
- < -6% TD, 10 min at 300 °F/149 °C, ASTM D1204
- <= +6% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 150 - 225% MD, ASTM D882
- 175 - 225% TD, ASTM D882
- Haze
- < 1%, ASTM D1003
- Modulus
- 1103 - 1379 MPa MD/TD Secant, ASTM D882
- 160,000 - 200,000 psi MD/TD Secant, ASTM D882
- Specific Gravity
- 2.11, ASTM D1505
- Surface Tension
- >= 42 dynes/cm (Treated Side), ASTM D2578
- Tensile Strength
- 28 - 48 MPa TD, ASTM D882
- 4000 - 7000 psi TD, ASTM D882
- 41 - 62 MPa MD, ASTM D882
- 6000 - 9000 psi MD, ASTM D882
- Water Vapor Transmission Rate
- 0.0008 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0015 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.0016 gms/100in²/day at 86 °F (30 °C), 60% RH, ASTM F1249
- 0.004 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.0057 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- 0.009 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.015 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.016 gms/m²/day at 86 °F (30 °C), 60% RH, ASTM F1249
- 0.048 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.065 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 4,380 in²/lb
- 6.23 m²/kg
Notes
- Test Conditions
- Test conditions for properties are 73°F, 50% RH unless otherwise noted
Sampling
- Sample Products
- Yes
- Crystalline Melting Point : 211 °C, ASTM D4591|412 °F, ASTM D4591
- Surface Tension : >= 42 dynes/cm (Treated Side), ASTM D2578
- Modulus : 1103 - 1379 MPa MD/TD Secant, ASTM D882|160,000 - 200,000 psi MD/TD Secant, ASTM D882
- Yield : 4,380 in²/lb|6.23 m²/kg
- Specific Gravity : 2.11, ASTM D1505
- Haze : < 1%, ASTM D1003
- Water Vapor Transmission Rate : 0.0008 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249|0.0015 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249|0.0016 gms/100in²/day at 86 °F (30 °C), 60% RH, ASTM F1249|0.004 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249|0.0057 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249|0.009 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249|0.015 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249|0.016 gms/m²/day at 86 °F (30 °C), 60% RH, ASTM F1249|0.048 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249|0.065 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Elongation : 150 - 225% MD, ASTM D882|175 - 225% TD, ASTM D882
- Tensile Strength : 28 - 48 MPa TD, ASTM D882|4000 - 7000 psi TD, ASTM D882|41 - 62 MPa MD, ASTM D882|6000 - 9000 psi MD, ASTM D882
- Dimensional Stability : < -6% TD, 10 min at 300 °F/149 °C, ASTM D1204|<= +6% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Test Conditions : Test conditions for properties are 73°F, 50% RH unless otherwise noted
- Sample Products : Yes