Aclar® Barrier Films
Aclar SupRx 900 (0.90 Mil/23 μm)
Aclar® SupRx 900 is a 0.90 mil (23 µm) PCTFE homopolymer, high performance barrier film for the pharma and medical markets. It offers increased moisture barrier over the Aclar® mid-barrier range.
Please sign in to access more documents
Once signed in, you may be able to access additional documents for your account.
With Aclar film, you can dial in the exact properties you need from several product grades so you have the optimum balance of performance and economics. When you also need oxygen and/or light barrier protection, Aclar film can be laminated to a wide range of substrates.
Honeywell has been supporting the pharmaceutical industry with Aclar film for more than 40 years.
Aclar high and ultra-high barrier films are usually selected for the most demanding applications, such as high moisture sensitivity or the need to pass the accelerated stability trials as set forth by ICH.
Properties
- Crystalline Melting Point
- 211 °C, ASTM D4591
- 412 °F, ASTM D4591
- Dimensional Stability
- < -12% TD, 10 min at 300 °F/149 °C, ASTM D1204
- <= +12% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 100 - 150% MD, ASTM D882
- 200 - 275% TD, ASTM D882
- Haze
- < 1% ASTM D1003
- Modulus
- 1138 - 1448 MPa TD Secant, ASTM D882
- 1310 - 1551 MPa MD Secant, ASTM D882
- 165000 - 210000 psi TD Secant, ASTM D882
- 190000 - 225000 psi MD Secant, ASTM D882
- Specific Gravity
- 2.11, ASTM D1505
- Surface Tension
- >= 42 dynes/cm (Treated Side), ASTM D2578
- Tensile Strength
- 11000 - 16000 psi MD, ASTM D882
- 41 - 55 MPa TD, ASTM D882
- 6000 - 7200 psi TD, ASTM D882
- 76 - 110 MPa MD, ASTM D882
- Water Vapor Transmission Rate
- 0.0018 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.003 gms/100in²/day at 86 °F (30 °C), 60% RH, ASTM F1249
- 0.0038 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.013 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.017 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- 0.028 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.047 gms/m²/day at 86 °F (30 °C), 60% RH, ASTM F1249
- 0.059 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.202 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.264 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 14595 in²/lb
- 20.75 m²/kg
Notes
- Test Conditions
- Test conditions for properties are 73°F, 50% RH unless otherwise noted
Sampling
- Sample Products
- Yes
Properties
- Crystalline Melting Point
- 211 °C, ASTM D4591
- 412 °F, ASTM D4591
- Dimensional Stability
- < -12% TD, 10 min at 300 °F/149 °C, ASTM D1204
- <= +12% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 100 - 150% MD, ASTM D882
- 200 - 275% TD, ASTM D882
- Haze
- < 1% ASTM D1003
- Modulus
- 1138 - 1448 MPa TD Secant, ASTM D882
- 1310 - 1551 MPa MD Secant, ASTM D882
- 165000 - 210000 psi TD Secant, ASTM D882
- 190000 - 225000 psi MD Secant, ASTM D882
- Specific Gravity
- 2.11, ASTM D1505
- Surface Tension
- >= 42 dynes/cm (Treated Side), ASTM D2578
- Tensile Strength
- 11000 - 16000 psi MD, ASTM D882
- 41 - 55 MPa TD, ASTM D882
- 6000 - 7200 psi TD, ASTM D882
- 76 - 110 MPa MD, ASTM D882
- Water Vapor Transmission Rate
- 0.0018 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.003 gms/100in²/day at 86 °F (30 °C), 60% RH, ASTM F1249
- 0.0038 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.013 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.017 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- 0.028 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.047 gms/m²/day at 86 °F (30 °C), 60% RH, ASTM F1249
- 0.059 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.202 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.264 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 14595 in²/lb
- 20.75 m²/kg
Notes
- Test Conditions
- Test conditions for properties are 73°F, 50% RH unless otherwise noted
Sampling
- Sample Products
- Yes
- Crystalline Melting Point : 211 °C, ASTM D4591|412 °F, ASTM D4591
- Yield : 14595 in²/lb|20.75 m²/kg
- Water Vapor Transmission Rate : 0.0018 gms/100in²/day at 77 °F (25 °C), 60% RH, ASTM F1249|0.003 gms/100in²/day at 86 °F (30 °C), 60% RH, ASTM F1249|0.0038 gms/100in²/day at 86 °F (30 °C), 65% RH, ASTM F1249|0.013 gms/100in²/day at 104 °F (40 °C), 75% RH, ASTM F1249|0.017 gms/100in²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249|0.028 gms/m²/day at 77 °F (25 °C), 60% RH, ASTM F1249|0.047 gms/m²/day at 86 °F (30 °C), 60% RH, ASTM F1249|0.059 gms/m²/day at 86 °F (30 °C), 65% RH, ASTM F1249|0.202 gms/m²/day at 104 °F (40 °C), 75% RH, ASTM F1249|0.264 gms/m²/day at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Tensile Strength : 11000 - 16000 psi MD, ASTM D882|41 - 55 MPa TD, ASTM D882|6000 - 7200 psi TD, ASTM D882|76 - 110 MPa MD, ASTM D882
- Surface Tension : >= 42 dynes/cm (Treated Side), ASTM D2578
- Specific Gravity : 2.11, ASTM D1505
- Modulus : 1138 - 1448 MPa TD Secant, ASTM D882|1310 - 1551 MPa MD Secant, ASTM D882|165000 - 210000 psi TD Secant, ASTM D882|190000 - 225000 psi MD Secant, ASTM D882
- Haze : < 1% ASTM D1003
- Elongation : 100 - 150% MD, ASTM D882|200 - 275% TD, ASTM D882
- Dimensional Stability : < -12% TD, 10 min at 300 °F/149 °C, ASTM D1204|<= +12% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Test Conditions : Test conditions for properties are 73°F, 50% RH unless otherwise noted
- Sample Products : Yes