Aclar Accel™ Barrier Films
Aclar Accel™ 5400
Honeywell Aclar Accel™ 5400 (5.40 mil/137 µm) is designed for opaque laminates and offers improved total cost effectiveness as compared to Cold Form Foil (CFF).
Please sign in to access more documents
Once signed in, you may be able to access additional documents for your account.
Properties
- Crystalline Melting Point
- 412°F, ASTM D4591
- Dimensional Stability
- < -2% TD, 10 min at 300 °F/149 °C, ASTM D1204
- <= +2% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 150 - 200% TD, ASTM D882
- 200 - 250% MD, ASTM D882
- Modulus
- 160,000 - 200,000 psi MD Secant, ASTM D882
- 160,000 - 200,000 psi TD Secant, ASTM D882
- Oxygen Transmission Rate
- 0.77 cc/100in² dbar at 73.4 °F (23 °C), 50% RH, ASTM D1927-20
- Specific Gravity
- 2.11 g/cm3
- Surface Tension
- ≥ 42 dynes/cm
- Tensile Strength
- 4,800 - 5,000 psi TD, ASTM D882
- 5,800 - 6,000 psi MD, ASTM D882
- Water Vapor Transmission Rate
- 0.0003 g/100in²d at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0007 g/100in²d at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.0022 g/100in²d at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.0030 g/100in²d at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 2,443 in2/lb
Sampling
- Sample Products
- Yes
Properties
- Crystalline Melting Point
- 412°F, ASTM D4591
- Dimensional Stability
- < -2% TD, 10 min at 300 °F/149 °C, ASTM D1204
- <= +2% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 150 - 200% TD, ASTM D882
- 200 - 250% MD, ASTM D882
- Modulus
- 160,000 - 200,000 psi MD Secant, ASTM D882
- 160,000 - 200,000 psi TD Secant, ASTM D882
- Oxygen Transmission Rate
- 0.77 cc/100in² dbar at 73.4 °F (23 °C), 50% RH, ASTM D1927-20
- Specific Gravity
- 2.11 g/cm3
- Surface Tension
- ≥ 42 dynes/cm
- Tensile Strength
- 4,800 - 5,000 psi TD, ASTM D882
- 5,800 - 6,000 psi MD, ASTM D882
- Water Vapor Transmission Rate
- 0.0003 g/100in²d at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0007 g/100in²d at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.0022 g/100in²d at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.0030 g/100in²d at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 2,443 in2/lb
Sampling
- Sample Products
- Yes
- Crystalline Melting Point : 412°F, ASTM D4591
- Yield : 2,443 in2/lb
- Water Vapor Transmission Rate : 0.0003 g/100in²d at 77 °F (25 °C), 60% RH, ASTM F1249|0.0007 g/100in²d at 86 °F (30 °C), 65% RH, ASTM F1249|0.0022 g/100in²d at 104 °F (40 °C), 75% RH, ASTM F1249|0.0030 g/100in²d at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Tensile Strength : 4,800 - 5,000 psi TD, ASTM D882|5,800 - 6,000 psi MD, ASTM D882
- Surface Tension : ≥ 42 dynes/cm
- Specific Gravity : 2.11 g/cm3
- Oxygen Transmission Rate : 0.77 cc/100in² dbar at 73.4 °F (23 °C), 50% RH, ASTM D1927-20
- Modulus : 160,000 - 200,000 psi MD Secant, ASTM D882|160,000 - 200,000 psi TD Secant, ASTM D882
- Elongation : 150 - 200% TD, ASTM D882|200 - 250% MD, ASTM D882
- Dimensional Stability : < -2% TD, 10 min at 300 °F/149 °C, ASTM D1204|<= +2% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Sample Products : Yes