Aclar Accel™ Barrier Films
Aclar Accel™ 1700
Honeywell Aclar Accel™ 1700 (1.70 mil/43 µm) provides an answer for cost-effective transparent films in the high moisture barrier range and is an appealing alternative to High Barrier (HB) PVdC.
Please sign in to access more documents
Once signed in, you may be able to access additional documents for your account.
Properties
- Crystalline Melting Point
- 412°F, ASTM D4591
- Dimensional Stability
- < -10% TD, 10 min at 300 °F/149 °C, ASTM D1204
- <= +12% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 175 - 250% MD, ASTM D882
- 250 - 300% TD, ASTM D882
- Modulus
- 170,000 - 200,000 psi MD Secant, ASTM D882
- 170,000 - 200,000 psi TD Secant, ASTM D882
- Oxygen Transmission Rate
- 2.86 cc/100in² dbar at 73.4 °F (23 °C), 50% RH, ASTM D1927-20
- Specific Gravity
- 2.11 g/cm3
- Surface Tension
- ≥ 42 dynes/cm
- Tensile Strength
- 5,000 - 8,000 psi TD, ASTM D882
- 9,000 - 12,000 psi MD, ASTM D882
- Water Vapor Transmission Rate
- 0.0011 g/100in²d at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0024 g/100in²d at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.0088 g/100in²d at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.0100 g/100in²d at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 7,723 in2/lb
Sampling
- Sample Products
- Yes
Properties
- Crystalline Melting Point
- 412°F, ASTM D4591
- Dimensional Stability
- < -10% TD, 10 min at 300 °F/149 °C, ASTM D1204
- <= +12% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Elongation
- 175 - 250% MD, ASTM D882
- 250 - 300% TD, ASTM D882
- Modulus
- 170,000 - 200,000 psi MD Secant, ASTM D882
- 170,000 - 200,000 psi TD Secant, ASTM D882
- Oxygen Transmission Rate
- 2.86 cc/100in² dbar at 73.4 °F (23 °C), 50% RH, ASTM D1927-20
- Specific Gravity
- 2.11 g/cm3
- Surface Tension
- ≥ 42 dynes/cm
- Tensile Strength
- 5,000 - 8,000 psi TD, ASTM D882
- 9,000 - 12,000 psi MD, ASTM D882
- Water Vapor Transmission Rate
- 0.0011 g/100in²d at 77 °F (25 °C), 60% RH, ASTM F1249
- 0.0024 g/100in²d at 86 °F (30 °C), 65% RH, ASTM F1249
- 0.0088 g/100in²d at 104 °F (40 °C), 75% RH, ASTM F1249
- 0.0100 g/100in²d at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Yield
- 7,723 in2/lb
Sampling
- Sample Products
- Yes
- Yield : 7,723 in2/lb
- Water Vapor Transmission Rate : 0.0011 g/100in²d at 77 °F (25 °C), 60% RH, ASTM F1249|0.0024 g/100in²d at 86 °F (30 °C), 65% RH, ASTM F1249|0.0088 g/100in²d at 104 °F (40 °C), 75% RH, ASTM F1249|0.0100 g/100in²d at 100 °F (37.8 °C), 100% RH, ASTM F1249
- Crystalline Melting Point : 412°F, ASTM D4591
- Oxygen Transmission Rate : 2.86 cc/100in² dbar at 73.4 °F (23 °C), 50% RH, ASTM D1927-20
- Dimensional Stability : < -10% TD, 10 min at 300 °F/149 °C, ASTM D1204|<= +12% MD, 10 min at 300 °F/149 °C, ASTM D1204
- Tensile Strength : 5,000 - 8,000 psi TD, ASTM D882|9,000 - 12,000 psi MD, ASTM D882
- Specific Gravity : 2.11 g/cm3
- Surface Tension : ≥ 42 dynes/cm
- Elongation : 175 - 250% MD, ASTM D882|250 - 300% TD, ASTM D882
- Modulus : 170,000 - 200,000 psi MD Secant, ASTM D882|170,000 - 200,000 psi TD Secant, ASTM D882
- Sample Products : Yes